== Description == | == Description == | ||
| − | [Abatron, Kenosha WI] A 2-part epoxy filled with microballoons | + | [Abatron, Kenosha WI] A structural adhesive putty composed 2-part epoxy filled with microballoons. WoodEpox® is a high-strength, no-shrink, lightweight, light-colored compound that can be used in any thickness to fill, replace, and repair wood and other materials. It can be painted, stained, sanded and worked like wood. WoodEpox® can be used for structures, floors, windowsills and frames, moldings, moldings, furniture and sculpture. In addition to wood, the product bonds well to ceramics, concrete, metal and glass. The working time is about 20 minutes. According to the manufacturer, WoodEpox® is 100% epoxy and contains no VOCs or water. A companion product, LiquidWood®, may be used for deeper penetration or as a priming layer. WoodEpox® is a permanent treatment for wood and cannot be safely removed. |
| + | [[[SliderGallery rightalign|Woodepox A FTIR.JPG~WoodEpox A FTIR|Woodepox B FTIR.JPG~WoodEpox B FTIR|Woodepox mix FTIR.JPG~WoodEpox mix FTIR]]] | ||
| − | + | == Risks == | |
| − | + | * WoodEpoxA is composed of a proprietary diglycidyl ether resin mixture with microballoons. The epoxy base material is a white thixotropic paste that is considered a minor skin irritant with low oral toxicity. | |
| − | + | * WoodEpoxB is composed of a proprietary mixture of amines mixed with microballoons. The curing agent is a tan thixotropic paste with a light ammonia odor. Contact may cause extreme eye irritation and minor skin irritation, including contact dermatitis. | |
| − | + | * Abatron WoodEpoxA and WoodEpoxB: [file:///C:/Users/mderr/Downloads/WoodEpox-SDS-3%20(1).pdf SDS] | |
| − | |||
| − | == | ||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| + | ==Physical and Chemical Properties== | ||
| + | WoodEpox® consists of 2 components: resin paste (A) and hardener paste (B). A well-blended mixture of equal proportions A and B will harden in 1-2 hours to form a lightweight, non-shrinking product that is resistant to chemical, water, heat, and weather. | ||
{| class="wikitable" | {| class="wikitable" | ||
|- | |- | ||
| − | ! scope="row"| | + | ! scope="row"| Product |
| − | | | + | | WoodEpox® mixture |
| + | |- | ||
| + | ! scope="row"| Form | ||
| + | | 100% solids, 1:1 mixture | ||
|- | |- | ||
| − | ! scope="row"| | + | ! scope="row"| Tensile Strength |
| − | | | + | | 17.5 Mpa |
|- | |- | ||
| − | ! scope="row"| | + | ! scope="row"| Compressive Strength |
| − | | | + | | 37.9 Mpa |
|- | |- | ||
| − | ! scope="row"| | + | ! scope="row"| Hardness Shore D |
| − | | | + | | 53-55 |
|- | |- | ||
| − | ! scope="row"| | + | ! scope="row"| Elongation |
| − | | | + | | 4% |
|} | |} | ||
| − | == | + | ==Resources and Citations== |
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | + | * Abatron : [https://www.abatron.com/product/woodepox/ WoodEpox] | |
| − | |||
| − | |||
| − | |||
| − | |||
Latest revision as of 12:05, 27 June 2022
Description
[Abatron, Kenosha WI] A structural adhesive putty composed 2-part epoxy filled with microballoons. WoodEpox® is a high-strength, no-shrink, lightweight, light-colored compound that can be used in any thickness to fill, replace, and repair wood and other materials. It can be painted, stained, sanded and worked like wood. WoodEpox® can be used for structures, floors, windowsills and frames, moldings, moldings, furniture and sculpture. In addition to wood, the product bonds well to ceramics, concrete, metal and glass. The working time is about 20 minutes. According to the manufacturer, WoodEpox® is 100% epoxy and contains no VOCs or water. A companion product, LiquidWood®, may be used for deeper penetration or as a priming layer. WoodEpox® is a permanent treatment for wood and cannot be safely removed.
Risks
- WoodEpoxA is composed of a proprietary diglycidyl ether resin mixture with microballoons. The epoxy base material is a white thixotropic paste that is considered a minor skin irritant with low oral toxicity.
- WoodEpoxB is composed of a proprietary mixture of amines mixed with microballoons. The curing agent is a tan thixotropic paste with a light ammonia odor. Contact may cause extreme eye irritation and minor skin irritation, including contact dermatitis.
- Abatron WoodEpoxA and WoodEpoxB: SDS
Physical and Chemical Properties
WoodEpox® consists of 2 components: resin paste (A) and hardener paste (B). A well-blended mixture of equal proportions A and B will harden in 1-2 hours to form a lightweight, non-shrinking product that is resistant to chemical, water, heat, and weather.
| Product | WoodEpox® mixture |
|---|---|
| Form | 100% solids, 1:1 mixture |
| Tensile Strength | 17.5 Mpa |
| Compressive Strength | 37.9 Mpa |
| Hardness Shore D | 53-55 |
| Elongation | 4% |
Resources and Citations
- Abatron : WoodEpox