Difference between revisions of "File:1 01 15 GessodOro EDS Spectrum.jpg"
(EDS Spectrum showing elemental peak height as a function of X-ray counts collected (LC) Elements Identified Major (> 10%): oxygen, carbon, calcium, sulfur Minor (1-10%): NA Trace (< 1%): NA Area X-ray counts collected: 1,018,003 Live Time: 35.8 sec...) |
|||
| Line 2: | Line 2: | ||
Elements Identified | Elements Identified | ||
| − | Major (> 10%): oxygen, carbon, calcium, sulfur | + | Major (> 10%): oxygen, carbon, calcium, sulfur. |
| − | Minor (1-10%): NA | + | Minor (1-10%): NA. |
| − | Trace (< 1%): NA | + | Trace (< 1%): NA. |
| − | Area X-ray counts collected: 1,018,003 | + | Area X-ray counts collected: 1,018,003. |
| − | Live Time: 35.8 seconds | + | Live Time: 35.8 seconds. |
| − | Magnification: 1384x | + | Magnification: 1384x. |
Analyzed using Oxford X-Max80 energy-dispersive X-Ray spectroscopy (EDS) and Oxford AZtec platform software. Pigment sample was applied to carbon tape and mounted onto aluminum examination stub. X-rays from sample were excited by a 20 kV SEM electron beam in a low vacuum chamber (10 Pascal). The resolution of the X-Max80 silicon drift detector is 123 eV at MnKα wavelength. | Analyzed using Oxford X-Max80 energy-dispersive X-Ray spectroscopy (EDS) and Oxford AZtec platform software. Pigment sample was applied to carbon tape and mounted onto aluminum examination stub. X-rays from sample were excited by a 20 kV SEM electron beam in a low vacuum chamber (10 Pascal). The resolution of the X-Max80 silicon drift detector is 123 eV at MnKα wavelength. | ||
Latest revision as of 09:22, 10 January 2017
EDS Spectrum showing elemental peak height as a function of X-ray counts collected (LC)
Elements Identified Major (> 10%): oxygen, carbon, calcium, sulfur. Minor (1-10%): NA. Trace (< 1%): NA.
Area X-ray counts collected: 1,018,003. Live Time: 35.8 seconds. Magnification: 1384x. Analyzed using Oxford X-Max80 energy-dispersive X-Ray spectroscopy (EDS) and Oxford AZtec platform software. Pigment sample was applied to carbon tape and mounted onto aluminum examination stub. X-rays from sample were excited by a 20 kV SEM electron beam in a low vacuum chamber (10 Pascal). The resolution of the X-Max80 silicon drift detector is 123 eV at MnKα wavelength.
File history
Click on a date/time to view the file as it appeared at that time.
| Date/Time | Thumbnail | Dimensions | User | Comment | |
|---|---|---|---|---|---|
| current | 08:39, 5 January 2017 |  | 1,460 × 441 (65 KB) | MKullman (talk | contribs) | EDS Spectrum showing elemental peak height as a function of X-ray counts collected (LC) Elements Identified Major (> 10%): oxygen, carbon, calcium, sulfur Minor (1-10%): NA Trace (< 1%): NA Area X-ray counts collected: 1,018,003 Live Time: 35.8 sec... |
You cannot overwrite this file.
File usage
The following page uses this file: