Difference between revisions of "Lascaux Acrylic Adhesive 360 HV"
(username removed) |
(username removed) |
||
| Line 1: | Line 1: | ||
== Description == | == Description == | ||
| − | [Alois K Diethelm, Switzerland] A trademark for a thermoplastic acrylic resin composed of a water-based dispersion of butyl acrylate and methylmethacrylate thickened with acrylic butylester. The minimum film formation temperature for Lascaux Acrylic Adhesive 360 HV is approximately | + | [Alois K Diethelm, Switzerland] A trademark for a thermoplastic acrylic resin composed of a water-based dispersion of butyl acrylate and methylmethacrylate thickened with acrylic butylester. The minimum film formation temperature for Lascaux Acrylic Adhesive 360 HV is approximately 0°C. It dries to form a film that is more flexible and elastic than 498HV. The dry film is slightly tacky and can be used as a weak pressure sensitive adhesive or it can be activated to improve adhesion with toluene, alcohol or heat (50-55°C). The emulsion can be thinned with water, but once the film is dried it is insoluble in water. Lascaux 360 HV is used as an adhesive for lining paintings and textiles. |
== Other Properties == | == Other Properties == | ||
| Line 15: | Line 15: | ||
== Additional Information == | == Additional Information == | ||
| − | Talas: [http://talasonline.com/photos/instructions/lascaux_adhesives.pdf Information sheet] | + | ° Talas: [http://talasonline.com/photos/instructions/lascaux_adhesives.pdf Information sheet] ° J. Down, M.MacDonald, J.Te'treault, S.Williams, Adhesive Testing at the Canadian Conservation Institute-An Evaluation of Selected Poly(Vinyl acetate) and Acrylic Adhesives", ''Studies in Conservation'' 41:19-44, 1996. ° D.Allard, K.Katz "Quantitative Study: The Effects of Sized Materials and Drying Time in the Use of Lascaux 360HV as a Lining Adhesive: ''JAIC'' 26;19-26, 1987 |
== Authority == | == Authority == | ||
| − | * | + | * Book and Paper Group, ''Paper Conservation Catalog'', AIC, 1984, 1989 |
* Product Information Comment: Manufacturer's literature: glass transition= -8; sealing point= 50-55C | * Product Information Comment: Manufacturer's literature: glass transition= -8; sealing point= 50-55C | ||
| − | * | + | * Marie Svoboda, Conservation Survey Index, unpublished, 1997 |
| − | * | + | * Gordon Hanlon, contributed information, 1998 |
| − | * | + | * Meredith Montague, contributed information, 1998 |
| − | * | + | * Teri Hensick, contributed information, 1998 |
| − | * | + | * Conservation Materials Ltd., Catalog |
| − | * | + | * Conservation Support Systems, Catalog, 1997 |
[[Category:Materials database]] | [[Category:Materials database]] | ||
Revision as of 06:29, 24 July 2013
Description
[Alois K Diethelm, Switzerland] A trademark for a thermoplastic acrylic resin composed of a water-based dispersion of butyl acrylate and methylmethacrylate thickened with acrylic butylester. The minimum film formation temperature for Lascaux Acrylic Adhesive 360 HV is approximately 0°C. It dries to form a film that is more flexible and elastic than 498HV. The dry film is slightly tacky and can be used as a weak pressure sensitive adhesive or it can be activated to improve adhesion with toluene, alcohol or heat (50-55°C). The emulsion can be thinned with water, but once the film is dried it is insoluble in water. Lascaux 360 HV is used as an adhesive for lining paintings and textiles.
Other Properties
Dry films: Soluble in acetone, ethanol, toluene and xylene. Insoluble in water, white spirit and ligroin.
| Molecular Weight | Tg= -8C |
|---|
Additional Information
° Talas: Information sheet ° J. Down, M.MacDonald, J.Te'treault, S.Williams, Adhesive Testing at the Canadian Conservation Institute-An Evaluation of Selected Poly(Vinyl acetate) and Acrylic Adhesives", Studies in Conservation 41:19-44, 1996. ° D.Allard, K.Katz "Quantitative Study: The Effects of Sized Materials and Drying Time in the Use of Lascaux 360HV as a Lining Adhesive: JAIC 26;19-26, 1987
Authority
- Book and Paper Group, Paper Conservation Catalog, AIC, 1984, 1989
- Product Information Comment: Manufacturer's literature: glass transition= -8; sealing point= 50-55C
- Marie Svoboda, Conservation Survey Index, unpublished, 1997
- Gordon Hanlon, contributed information, 1998
- Meredith Montague, contributed information, 1998
- Teri Hensick, contributed information, 1998
- Conservation Materials Ltd., Catalog
- Conservation Support Systems, Catalog, 1997