− | + | EDS Spectrum showing elemental peak height as a function of X-ray counts collected (LC) | |
+ | |||
+ | Elements Identified | ||
+ | Major (> 10%): carbon, oxygen. | ||
+ | Minor (1-10%): silicon, iron, calcium, aluminum, potassium. | ||
+ | Trace (< 1%): magnesium. | ||
+ | |||
+ | Area X-ray counts collected: 1,045,332. | ||
+ | Live Time: 17.4 seconds. | ||
+ | Magnification: 1707x. | ||
+ | Analyzed using Oxford X-Max80 energy-dispersive X-Ray spectroscopy (EDS) and Oxford AZtec platform software. Pigment sample was applied to carbon tape and mounted onto aluminum examination stub. X-rays from sample were excited by a 20 kV SEM electron beam in a low vacuum chamber (10 Pascals). The resolution of the X-Max80 silicon drift detector is 123 eV at MnKα wavelength. |
Latest revision as of 15:21, 6 July 2017
EDS Spectrum showing elemental peak height as a function of X-ray counts collected (LC)
Elements Identified Major (> 10%): carbon, oxygen. Minor (1-10%): silicon, iron, calcium, aluminum, potassium. Trace (< 1%): magnesium.
Area X-ray counts collected: 1,045,332. Live Time: 17.4 seconds. Magnification: 1707x. Analyzed using Oxford X-Max80 energy-dispersive X-Ray spectroscopy (EDS) and Oxford AZtec platform software. Pigment sample was applied to carbon tape and mounted onto aluminum examination stub. X-rays from sample were excited by a 20 kV SEM electron beam in a low vacuum chamber (10 Pascals). The resolution of the X-Max80 silicon drift detector is 123 eV at MnKα wavelength.
File history
Click on a date/time to view the file as it appeared at that time.
Date/Time | Thumbnail | Dimensions | User | Comment | |
---|---|---|---|---|---|
current | 15:17, 6 July 2017 | 1,688 × 442 (80 KB) | AJones (talk | contribs) | File uploaded with MsUpload |
You cannot overwrite this file.
File usage
The following page uses this file: