| − | + | EDS Spectrum showing elemental peak height as a function of X-ray counts collected (LC) | |
| + | |||
| + | Elements Identified | ||
| + | Major (> 10%): cadmium, carbon, oxygen. | ||
| + | Minor (1-10%): sulfur. | ||
| + | Trace (< 1%): NA. | ||
| + | |||
| + | Area X-ray counts collected: 1,012,720. | ||
| + | Live Time: 19.5 seconds. | ||
| + | Magnification: 2208x. | ||
| + | Analyzed using Oxford X-Max80 energy-dispersive X-Ray spectroscopy (EDS) and Oxford AZtec platform software. Pigment sample was applied to carbon tape and mounted onto aluminum examination stub. X-rays from sample were excited by a 20 kV SEM electron beam in a low vacuum chamber (10 Pascals). The resolution of the X-Max80 silicon drift detector is 123 eV at MnKα wavelength. | ||
Latest revision as of 15:27, 15 August 2017
EDS Spectrum showing elemental peak height as a function of X-ray counts collected (LC)
Elements Identified Major (> 10%): cadmium, carbon, oxygen. Minor (1-10%): sulfur. Trace (< 1%): NA.
Area X-ray counts collected: 1,012,720. Live Time: 19.5 seconds. Magnification: 2208x. Analyzed using Oxford X-Max80 energy-dispersive X-Ray spectroscopy (EDS) and Oxford AZtec platform software. Pigment sample was applied to carbon tape and mounted onto aluminum examination stub. X-rays from sample were excited by a 20 kV SEM electron beam in a low vacuum chamber (10 Pascals). The resolution of the X-Max80 silicon drift detector is 123 eV at MnKα wavelength.
File history
Click on a date/time to view the file as it appeared at that time.
| Date/Time | Thumbnail | Dimensions | User | Comment | |
|---|---|---|---|---|---|
| current | 15:24, 15 August 2017 |  | 1,688 × 442 (76 KB) | AJones (talk | contribs) | File uploaded with MsUpload |
You cannot overwrite this file.
File usage
The following page uses this file: