==Description==   
 
==Description==   
A lightweight, ‘bubbly’ form of concrete commonly used in construction between the 1950s and mid-1990s. Reinforced Autoclaved Aerated Concrete (RAAC) was predominantly found as precast panels in roofs (commonly flat roofs, sometimes pitched) and occasionally in floors and walls. RAAC panels are light-grey or white in appearance, the underside of the panels will appear smooth. The inside of the planks will appear bubbly, often described as looking like an Aero bar. Unlike traditional concrete, there will not be visible stones (aggregate) in the panels. The panels have distinctive V-shaped grooves at at the connection points (every 600 mm).
+
A lightweight, ‘bubbly’ form of concrete masonry blocks and pre-cast panels commonly used in construction between the 1950s and mid-1990s. Autoclaved Aerated Concrete (AAC) was made using a fine aggregate mixed with chemicals to create gas bubbles then cast with a metal reinforcement (RAAC) network and cured with high heat. The result was a relatively weak concrete that had poor load-bearing ability and weak bonding with its embedded metal reinforcement. RAAC pre-cast panels were predominantly used in roofs (commonly flat roofs, sometimes pitched) and occasionally in floors and walls. The panels are light-grey or white in appearance, with a smooth, paintable surface. The inside of the planks will appear bubbly, often described as looking like an Aero bar. Unlike traditional concrete, there will not be visible stones (coarse aggregate) in the panels. The panels have distinctive V-shaped grooves at at the connection points (every 600 mm).  A bituminous or latex coating was sometimes added as a water barrier.
  
 
== Synonyms and Related Terms ==
 
== Synonyms and Related Terms ==
RAAC
+
RAAC; Reinforced AAC
 +
             
 +
==Risks== 
 +
* Cracking and spalling   
 +
* Load-bearing failure
 +
* Corrosion of reinforcement bars
 +
* Movement and deflections of panels
  
==Applications==       
 
==Working Properties==               
 
==Risks==       
 
* Failure
 
==Physical and Chemical Properties==
 
 
==Forms and Sizes==
 
==Forms and Sizes==
 
* Typically 600 mm wide panels
 
* Typically 600 mm wide panels
 +
 
==Resources and Citations==
 
==Resources and Citations==
 
* Conservation Distlist: [https://community.culturalheritage.org/discussion/raac-concrete RAAC concrete thread] Accessed August 2023
 
* Conservation Distlist: [https://community.culturalheritage.org/discussion/raac-concrete RAAC concrete thread] Accessed August 2023

Revision as of 07:46, 12 September 2023

RAAC ceiling Panels
Department of Education (UK) report: RAAC Guide
RAAC wsll panels
Department of Education (UK) report: RAAC Guide
RAAC fragment
Department of Education (UK) report: RAAC Guide

Description

A lightweight, ‘bubbly’ form of concrete masonry blocks and pre-cast panels commonly used in construction between the 1950s and mid-1990s. Autoclaved Aerated Concrete (AAC) was made using a fine aggregate mixed with chemicals to create gas bubbles then cast with a metal reinforcement (RAAC) network and cured with high heat. The result was a relatively weak concrete that had poor load-bearing ability and weak bonding with its embedded metal reinforcement. RAAC pre-cast panels were predominantly used in roofs (commonly flat roofs, sometimes pitched) and occasionally in floors and walls. The panels are light-grey or white in appearance, with a smooth, paintable surface. The inside of the planks will appear bubbly, often described as looking like an Aero bar. Unlike traditional concrete, there will not be visible stones (coarse aggregate) in the panels. The panels have distinctive V-shaped grooves at at the connection points (every 600 mm). A bituminous or latex coating was sometimes added as a water barrier.

Synonyms and Related Terms

RAAC; Reinforced AAC

Risks

  • Cracking and spalling
  • Load-bearing failure
  • Corrosion of reinforcement bars
  • Movement and deflections of panels

Forms and Sizes

  • Typically 600 mm wide panels

Resources and Citations

Retrieved from "https://cameo.mfa.org/index.php?title=Reinforced_autoclaved_aerated_concrete&oldid=96456"