Nylon 6T is made by polymerizing hexamethylene diamine with terephthalic acid. Nylon 6T is similar in most properties to nylon 6 and 6,6, but it has a higher melting point and greater density. Nylon 6T also has good heat resistance and resistance to stretch. It is most often used as a precursor for producing aramid fibers. | Nylon 6T is made by polymerizing hexamethylene diamine with terephthalic acid. Nylon 6T is similar in most properties to nylon 6 and 6,6, but it has a higher melting point and greater density. Nylon 6T also has good heat resistance and resistance to stretch. It is most often used as a precursor for producing aramid fibers. | ||
| − | See [ | + | See [[nylon%20fiber|nylon fiber]]. |
== Synonyms and Related Terms == | == Synonyms and Related Terms == | ||
| Line 9: | Line 9: | ||
polyhexamethylene terephthalamide | polyhexamethylene terephthalamide | ||
| − | == | + | ==Physical and Chemical Properties== |
| − | Moisture regain = 4.5% | + | * Moisture regain = 4.5% |
| + | * Melting Point = 370 C | ||
| + | * Density = 1.21 g/ml | ||
| − | + | ==Resources and Citations== | |
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | + | * Marjory L. Joseph, ''Introductory Textile Science'', Holt, Rinehart and Winston, Fort Worth, TX, 1986, p. 135. | |
| − | + | * J.Gordon Cook, ''Handbook of Textile Fibres:II Man-made Fibres'', Merrow Publishing Co. , Durham, England, 1984, p.324. | |
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
[[Category:Materials database]] | [[Category:Materials database]] | ||
Latest revision as of 13:51, 20 October 2022
Description
Nylon 6T is made by polymerizing hexamethylene diamine with terephthalic acid. Nylon 6T is similar in most properties to nylon 6 and 6,6, but it has a higher melting point and greater density. Nylon 6T also has good heat resistance and resistance to stretch. It is most often used as a precursor for producing aramid fibers.
See Nylon fiber.
Synonyms and Related Terms
polyhexamethylene terephthalamide
Physical and Chemical Properties
- Moisture regain = 4.5%
- Melting Point = 370 C
- Density = 1.21 g/ml