| − | Nylon PACM-12 is made from bis(p-aminocyclohexyl) methane polymerized with dodecanedioic acid. PACM-12 fibers have a luxurious feel and excellent durability. They were originally produced under the brand name [ | + | Nylon PACM-12 is made from bis(p-aminocyclohexyl) methane polymerized with dodecanedioic acid. PACM-12 fibers have a luxurious feel and excellent durability. They were originally produced under the brand name [[Qiana|Qiana®]] but are no longer commercially made. |
| − | See [ | + | See [[nylon%20fiber|nylon fiber]]. |
== Synonyms and Related Terms == | == Synonyms and Related Terms == | ||
| Line 9: | Line 9: | ||
Qiana® | Qiana® | ||
| − | == | + | == Physical and Chemical Properties == |
| − | Tenacity = 3.5 g/denier Elongation = 20-30% Moisture regain = 2.0-2.5% | + | * Tenacity = 3.5 g/denier |
| + | * Elongation = 20-30% | ||
| + | * Moisture regain = 2.0-2.5% | ||
| + | * Melting Point = 275 | ||
| + | * Density = 1.03 | ||
| − | + | == Resources and Citations == | |
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
| − | |||
* Marjory L. Joseph, ''Introductory Textile Science'', Holt, Rinehart and Winston, Fort Worth, TX, 1986 | * Marjory L. Joseph, ''Introductory Textile Science'', Holt, Rinehart and Winston, Fort Worth, TX, 1986 | ||
Latest revision as of 08:01, 21 October 2020
Description
Nylon PACM-12 is made from bis(p-aminocyclohexyl) methane polymerized with dodecanedioic acid. PACM-12 fibers have a luxurious feel and excellent durability. They were originally produced under the brand name Qiana® but are no longer commercially made.
See Nylon fiber.
Synonyms and Related Terms
Qiana®
Physical and Chemical Properties
- Tenacity = 3.5 g/denier
- Elongation = 20-30%
- Moisture regain = 2.0-2.5%
- Melting Point = 275
- Density = 1.03